Adhesive bonding of glassy polymer surfaces by an ultrathin layer of a semicrystalline polymer

To develop a greater understanding of interfacial interactions between a semicrystalline polymer and a glassy polymer, adhesion tests were performed on very thin layers of poly(ethylene oxide) (PEO) sandwiched between two layers of poly(tetramethyl bisphenol A polycarbonate) (TMPC). The tests were designed to provide intimate contact between the surfaces while they were heated above the melting point of the PEO and cooled back to room temperature. A contact mechanics approach, based on the Johnson, Kendall, and Roberts theory, was used to determine values of the energy release rate describing the energetic driving force for crack propagation within the interfacial region. The ability to measure crack propagation at large values of the energy release rate was limited by rupture of the silicone elastomer that was used to provide a sufficiently compliant matrix for the adhesion experiment. By cycling the tensile stress at relatively low loading levels, we were able to measure fatigue crack propagation at values of the energy release rate that did not result in failure of the elastomer. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3809–3821, 2004     

Synthesis and characterization of soluble polyimides containing trifluoromethyl groups in their backbone

A series of polyimides were synthesized from 2,2‐Bis(3,4‐dicarboxyphenyl)hexafluoropropane, 2,2‐bis(3‐amino‐4‐hydroxyphenyl)‐hexafluoropropane, and 4,4′‐oxydianiline by chemical imidization. The effects of the diamine ratios on the properties of the films were evaluated through the study of their thermal, electrical, and morphological properties. All the polymers exhibited better solubility in most of the organic solvents and hence were easily processable. Polyimides with more 2,2‐bis(3‐amino‐4‐hydroxyphenyl)‐hexafluoropropane exhibited better solubility and a low refractive index, which is highly desired for microelectronic applications. The dielectric constant and birefringence were strongly dependent on the fluorine content. With an increase in the fluorine substitution, both the dielectric constant and birefringence decreased. All the polymers exhibited high thermal stability (>400 °C). The absence of crystalline melting in differential scanning calorimetry and broad wide‐angle X‐ray diffraction patterns revealed the amorphous nature of the polymers, which was due to the presence of bulky CF₃ groups and hinged ether linkages of the diamine component. The residual stress values decreased with an increase in the 4,4′‐oxydianiline content, and the results were in agreement with the dielectric constant. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4303–4312, 2004     

Changes in the near-edge X-ray absorption fine structure spectra of long-chain diacetylene derivatives through photopolymerization in Langmuir–Blodgett films

Photopolymerization of cadmium 10,12-pentacosadiynoate (CdDA) in Langmuir–Blodgett (LB) films, with the molecular packing well arranged by moderate preannealing, was investigated with near-edge X-ray absorption fine structure (NEXAFS) spectroscopy. Greenish films of polydiacetylene with an absorption wavelength of 705 nm were obtained through the photopolymerization of preannealed monomer LB films, and this resulted in an extended π-conjugate system based on the well-ordered monomer in a two-dimensional arrangement. The electronic structures of the polydiacetylenes were found to be correlated to the variation of the molecular arrangements in the films from the changes in the NEXAFS spectra through photopolymerization in the LB films. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2329–2336, 2004     

Control of self‐organized low‐dimensional morphology in poly(styrene‐b‐4vinylpyridine)/polystyrene blend thin films

The surface morphologies of poly(styrene‐b‐4vinylpyridine) (PS‐b‐P4VP) diblock copolymer and homopolystyrene (hPS) binary blend thin films were investigated by atomic force microscopy as a function of total volume fraction of PS (?_PS) in the mixture. It was found that when hPS was added into symmetric PS‐b‐P4VP diblock copolymers, the surface morphology of this diblock copolymer was changed to a certain degree. With ?_PS increasing at first, hPS was solubilized into the corresponding domains of block copolymer and formed cylinders. Moreover, the more solubilized the hPS, the more cylinders exist. However, when the limit was reached, excessive hPS tended to separate from the domains independently instead of solubilizing into the corresponding domains any longer, that is, a macrophase separation occurred. A model describing transitions of these morphologies with an increase in ?_PS is proposed. The effect of composition on the phase morphology of blend films when graphite is used as a substrate is also investigated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3496–3504, 2004     

Novel fixed‐site–carrier polyvinylamine membrane for carbon dioxide capture

Fixed‐site–carrier membranes were prepared for the facilitated transport of CO₂ by casting polyvinylamine (PVAm) on various supports, such as poly(ether sulfone) (PES), polyacrylonitrile (PAN), cellulose acetate (CA), and polysulfone (PSO). The cast PVAm on the support was crosslinked by various methods with glutaraldehyde, hydrochloric acid, sulfuric acid, and ammonium fluoride. Among the membranes tested, the PVAm cast on polysulfone and crosslinked by ammonium fluoride showed the highest selectivity of CO₂ over CH₄ (>1000). The permeance of CO₂ was then measured to be 0.014 m³ (STP)/(m² bar h) for a 20 μm thick membrane. The effect of the molecular weight of PVAm and feed pressure on the permeance was also investigated. The selectivity increased remarkably with increasing molecular weight and decreased slightly with increased pressure in the range of 1 to 4 bar. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4326–4336, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

密封容器中后处理制备Tl2Ba2CaCu2Oy高温超导薄膜及其性能研究

以铝酸镧（001）单晶为基片，采用两步法制备Tl2Ba2CaCu2Oy（Tl 2212）高 温超导薄膜.首先，利用脉冲激光沉积（PLD）工艺沉积Ba2CaCu2Ox非晶前驱体薄膜；然后，前驱体薄膜在高温（720—850℃）下密封钢容器里铊化结晶形成Tl 2212薄膜.XRD结果表明Tl2212 薄膜是沿c轴方向生长的，其相组成为Tl 2212，摇摆曲线（0012）的半高宽为0.72° ，SEM图像显示其表面光滑平整，其零电阻温度为106.2K. 关键词： Tl 2212超导薄膜 脉冲激光沉积     

薄膜外延生长的计算机模拟

以Cu膜为例，用Monte-Carlo算法模拟了薄膜生长的随机过程，并提出了更加完善的模型.在合理选择原子间相互作用计算方法的基础上，考虑了原子的吸附、在生长表面的迁移及迁移所引起的近邻原子连带效应、从生长表面的脱附等过程.模拟计算了薄膜的早期成核情况以及表面粗糙度和相对密度.结果表明，随着衬底温度的升高或入射率的降低，沉积在衬底上的原子逐步由离散型分布向聚集状态过渡形成一些岛核，并且逐步由二维岛核向三维岛核过渡.在一定的原子入射率下，存在三个优化温度，成核率最高时的最大成核温度Tn、薄膜的表面粗糙度最低 关键词： Monte-Carlo算法 计算机模拟 薄膜生长     

多壁碳纳米管膜湿敏特性的研究

研究了多壁碳纳米管(MWNTs)薄膜的湿敏特性，实验所用的多壁碳纳米管是用热灯丝化学气相沉积法(CVD)合成的.分别对未修饰和修饰的多壁碳纳米管膜温度和湿度特性进行研究后发现，修饰的多壁碳纳米管对温度和湿度非常敏感，且对湿度的响应时间和恢复时间短，重复性好.而未修饰的多壁碳纳米管对温度和湿度不太敏感.对修饰多壁碳纳米管的湿敏特性进行了理论分析，给出了其理论表示式. 关键词： 多壁碳纳米管 化学修饰 湿敏特性 物理吸附     

采用空心阴极放电等离子体化学气相沉积方法制备a-CH薄膜

 研究了不同衬底-阴极距离、直流电压和H₂流量对a-CH薄膜沉积速率的影响。结果表明：衬底-阴极距离必须大于0.5cm，随着该距离的增加，薄膜的沉积速率减少；直流电压达550V时沉积速率最大；随着H2含量的增加，CH₄含量相对减少，沉积速率随之降低。用AFM观察了以该方法制得的448.4nm CH薄膜的表面形貌，表面粗糙度约为10nm。最后测出了不同条件下CH薄膜的UV-VIS谱，由此可以计算得到薄膜的禁带宽度及折射率。